Aluminium extrusion
- individual development and production of aluminium extrusion profiles for our customers
- production of aluminium extrusion profiles in accordance with customer specifications (drawings, diagrams)
- hollow profiles
- flat profiles
- short delivery times
- use of various alloys, such as EN AW 6060, EN AW 6063, AN AW 6101B, EN AW 6005 A, EN AW 6082 with different strengths (see table)
- the length of the profiles depends on the profile width, profile weight and profile shape; in principle lengths up to 12.0 m are possible; shorter lengths are enabled on a separate saw
- the length tolerances are inline 0/+10 mm; tighter tolerances
- we extrude in accordance with the strictest standards EN 755-9 and EN 12020-2
- ISO 9001:2008 certified production
- wall thicknesses from min. 0.8 mm (12 MN extruder) or 1.3 mm (25 MN extruder) are possible
- as profile weight we implement 50 gr/RM to 2.0 kg/RM (12 MN extruder) and 1.0 kg to 15.0 kg/RM (25 MN extruder)
We process the following alloys on our production plant:
Material designation | Mechanical properties | ||||||
Alloy designation | Alloy | Strength | Tensile strength Rm (N/mm²) min. | 0.2% permanent elongation limit Rp0.2 min. | breaking elongation | Brinell approx. | Notes on condition |
EN AW 6060 | AlMgSi0,5 | F13/T4 | 120 N/mm² | 60 N/mm² | 16% | 45 HB | cold cured |
EN AW 6060 | AlMgSi0,5 | F18/T64 | 180 N/mm² | 80 N/mm² | 12% | 45 HB |
|
EN AW 6060 | AlMgSi0,5e ≤ 3 mm3 mm < e ≤ 25 mm | F22/T66 | 215 N/mm² | 160 N/mm² | 8% | 70 HB | hotcured |
EN AW 6063 | AlMgSi0,7 | F25/T66 | 260 N/mm² | 240 N/mm² | 10% | 86 HB | hot cured |
EN AW 6101B | AlMgSi0,5 | F22/T6 | 215 N/mm² | 160 N/mm² | 8% | 70 HB |
|
EN AW 6005A | AlMgSi0,7 | F17/T4 | 180 N/mm² | 90 N/mm² | 15% | 54 HB | cold cured |
EN AW 6005A | AlMgSi0,7 | F26/T6 | 260 N/mm² | 215 N/mm² | 8% | 85 HB | hot cured |
EN AW 6082 | AlMgSi1 | F21/T4 | 205 N/mm² | 110 N/mm² | 14% | 65 HB | cold cured |
EN AW 6082 | AlMgSi1 | F28/T66 | 275 N/mm² | 200 N/mm² | 8% | 80 HB | hot cured |
EN AW 6082 | AlMgSi1e ≤ 5 mm | F28/T66 | 290 N/mm² | 250 N/mm² | 8% | 90 HB | hot cured |
e = wall thickness, Other alloys upon request.